c100 carbon steel

 C100 steel is a high-level high-carbon tool steel, the advantages are good machinability, cheap price, easy

 source, but low hardenability, poor wear resistance, quenching deformation. Because the steel contains few

 alloying elements, the tempering resistance is low, and the hardening layer is shallow, so its carrying capacity is

 low. Although the workpiece has high hardness and wear resistance, the toughness of the workpiece with small

 section is insufficient, and the forge with large section has a tendency to retain mesh carbide. The minimum

 heating temperature of complete globalization is 740℃, the best isothermal temperature is 690 ~ 720℃, the

 heating temperature of flake carbide is 780℃, and the heat softening temperature is 250℃. The hardening

 depth is 15 ~ 18mm for water quenching and 5 ~ 7mm for oil quenching. The steel is roughed in an annealed

 state, then quenched at low temperature and tempered to high hardness, and then finished. High wear

 resistance and mirror finish are obtained. Low carbon martensite quenching, so that the mold has high wear

 resistance and toughness, prevent and reduce deformation and cracking phenomenon.

Its remarkable characteristics are pure steel, uniform organization, good crystal refinement, excellent impact resistance of the cutting edge, convenient grinding belongs to low-carbon stainless steel.

100c is also high carbon steel, the carbon content is greater than 82a, the carbon content is 1%, the hardness is higher than 82a, in addition to ensuring the chemical composition and mechanical properties, do the impact test when the temperature is 0 degrees.

C100 steel is a high-level high-carbon tool steel, the advantages are good machinability, cheap price, easy source, but low hardenability, poor wear resistance, quenching deformation.

Because the steel contains few alloying elements, the tempering resistance is low, and the hardening layer is shallow, so its carrying capacity is low. Although the workpiece has high hardness and wear resistance, the toughness of the workpiece with small section is insufficient, and the forge with large section has a tendency to retain mesh carbide.

The minimum heating temperature of complete globalization is 740℃, the best isothermal temperature is 690 ~ 720℃, the heating temperature of flake carbide is 780℃, and the heat softening temperature is 250℃. The hardening depth is 15 ~ 18mm for water quenching and 5 ~ 7mm for oil quenching.